As a dark horse in the building materials industry, the aluminum composite panel is increasingly favored by consumers due to its diverse varieties and extensive use. In this post, I will introduce a fire-rated aluminum composite panel. I hope this post can give you some advice if you have a fireproof requirements.
Fire-rated aluminum composite panel refers to that aluminum composite panel is adopted flame-retardant core material, and the combustion performance of the product reaches the refractory grade (class B1) or non-combustible grade (class A); At the same time, other performance indicators must also meet the technical specifications of aluminum composite panels.
For B1 grade plastic core, it contains 55% – 55% flame retardant, the main ingredients are aluminum oxide (Al₂O₃) and magnesium oxide (MgO) ;
A2 grade plastic core material: It Contains 88% – 90% of the flame retardant, the main ingredients are aluminum hydroxide(Al(OH)3) and magnesium hydroxide (Mg(OH)2) ;
For B1 grade panels: When B1 grade panels are put on fire, it can be cached on fire after 5 minutes, and the fire will extinguish after 10 seconds when the fire leave the panels. While for A2 grade fire-rated aluminum composite panels, it can be cached on fire after 20 minutes, and the fire will extinguish immediately when the fire leave the panels.
(1) According to GB/T8625-88 test, the average residual length of each set of specimens ≥ 150mm, (the remaining length of each specimen> 0), and the average peak temperature of each test flue gas temperature ≤ 200 °C;
(2) According to GB/T 8626-88 test, height index of flame tip <150mm, and the phenomenon of ignition of filter paper by burning drips is not allowed;
(3) According to GB/T8627-1999 test, smoke density rating (SDR) ≤ 75.
(1)According to GB/T 8625-88 test , the average residual length of each set of specimens ≥ 350mm (the remaining length of any specimen is > 200mm), and the peak value of the average flue gas temperature for each test ≤ 125° No burning phenomenon on the back of the specimen;
(2)According to GB/T8627-1999 test, smoke density rating (SDR) ≤ 15;
(3) According to GB/T14402-93 and GB/T14403-93 test, the thermal value of its material ≤ 4.2MJ/kg, the heat released per unit area of the test piece ≤ 16.8MJ/m2;
(4)According to GA 132–1996, the total non-lethal concentration of Lco in flue gas toxicity of burning materials is greater than or equal to 25.0 mg/L, and the mice will not die within 3 days after exposure and their weight will be recovered.
B1 grade aluminium composite panel: Although not strictly referred to as Non-combustible ,it has a very low spread of flame indices and will not contribute to the spread of flame. Therefore, this type of panel may be used on high rise buildings. It must be attached to a fire rated wall.
A2 grade aluminum composite panel:
This type of panel is Non-combustible, which may be used on high rise buildings. It must be attached to a fire-rated wall.
Alumibond aluminum composite panel has always been a leader in the domestic aluminum composite panel industry, but at present, we cannot produce mature A2 grade fire-rated aluminum composite panels in our Singapore market. But as our experience, the most popular fire-resistant grade for all customers is B1 grade, the price and quality is most cost-effective for them, in addition, our B1 grade aluminum composite panel enjoys a high reputation both at home and abroad. We are willing to do our best to provide you with the best service. Contact us today for free quote